ANALISIS LAJU KOROSI BAJA KARBON ST 60 TERHADAP LARUTAN HIDROGEN KLORIDA (HCl) DAN LARUTAN NATRIUM HIDROKSIDA (NaOH)

MUHAMAD RUSDI WILDANURDI KHASIBUDIN, MUHAMAD RUSDI WILDANURDI KHASIBUDIN (2019) ANALISIS LAJU KOROSI BAJA KARBON ST 60 TERHADAP LARUTAN HIDROGEN KLORIDA (HCl) DAN LARUTAN NATRIUM HIDROKSIDA (NaOH). Bachelor thesis, UNIVERSITAS ISLAM MAJAPAHIT MOJOKERTO.

[img] Text
(JURNAL MUHAMAD RUSDI W.K).pdf

Download (461kB)
[img] Text
BAB I.pdf

Download (89kB)
[img] Text
BAB II.pdf

Download (493kB)
[img] Text
BAB III.pdf
Restricted to Repository staff only

Download (462kB)
[img] Text
BAB IV.pdf
Restricted to Repository staff only

Download (511kB)
[img] Text
BAB V.pdf

Download (141kB)

Abstract

ABSTRAK Khasibudin, Muhamad Rusdi Wildanurdi, 2018. Analisis Laju Korosi Baja Karbon St 60 Terhadap Larutan Hidrogen Klorida (HCl) Dan Larutan Natrium Hidroksida (NaOH). Skripsi / tugas akhir, Program Studi Teknik Mesin, Fakultas Teknik Mesin, Universitas Islam Majapahit (UNIM). Pembimbing I : Dicki Nizar Z, ST., MT. Pembimbing II : Rahmad Kusbiyantoro, ST., MT. Korosi merupakan kerusakan material logam yang disebabkan reaksi antara logam dengan lingkungannya yang menghasilkan oksida logam, sulfida logam atau hasil reaksi lainnya yang lebih dikenal sebagai pengkaratan. Baja adalah logam paduan dengan besi sebagai unsur dasar dan karbon sebagai unsur paduan utamanya. Kandungan karbon dalam baja berkisar antara 0.2% hingga 2.1% berat sesuai ukurannya. Penelitian ini menggunakan metode eksperimen. Objek penelitian menggunakan plat baja karbon st 60 dengan ukuran spesimen 28 mm x 18 mm x 3 mm. Spesimen yang diujikan dalam penelitian ini ada 8 spesimen yang akan mendapatkan perlakuan berbeda yaitu berbeda variasi waktu dan jenis pH yang berbeda. Menggunakan metode perendaman spesimen dalam wadah uji dengan volume 50 ml dari setiap wadah uji. Dilakukan uji fisik untuk mengetahui perbedaan dari baja karbon yang belum terkorosi dengan baja karbon yang terkorosi, dan uji berat untuk mengetahui perbandingan berat spesimen awal dan spesimen akhir. Untuk perendaman dalam larutan HCl dengan pH 2 laju korosi terbesarnya adalah 22,903 mmpy. Sedangkan untuk perendaman dalam larutan NaOH dengan pH 13 laju korosi terbesarnya adalah 0,036 mmpy. Untuk perendaman dalam larutan HCl dan larutan NaOH laju korosi terbesarnya terjadi pada hari ke 2 saat pengujian dengan larutan HCl dan laju korosi terbesarnya pada hari ke 3 saat pengujian dengan larutan NaOH. Sedangkan laju korosi terkecil sebesar 12,785 mmpy yang di uji menggunakan larutan HCl terjadi pada hari ke 4 pengujian dan laju korosi terkecil sebesar 0,032 mmpy yang di uji mengunakan larutan NaOH terjadi pada hari ke 1 pengujian. Waktu dan pH berpengaruh terhadap laju korosi. Laju korosi terbesar terjadi pada pH asam. Kata kunci : Korosi, St 60, HCl, NaOH. ABSTRACT Khasibudin, Muhamad Rusdi Wildanurdi, 2018. Analysis of Corrosion Rates of St 60 Carbon Steels Against Hydrogen Chloride Solutions (HCl) And Sodium Hydroxide Solutions (NaOH). Thesis / final project, Mechanical Engineering Study Program, Faculty of Mechanical Engineering, Majapahit Islamic University (UNIM). Counselor I : Dicki Nizar Z, ST., MT. Counselor II : Rahmad Kusbiyantoro, ST., MT. Corrosion is the damage of metal material caused by a reaction between metal and its environment which produces metal oxides, metal sulfides or other reactions which are better known as rusting. Steel is a metal alloy with iron as a basic element and carbon as its main alloying element. The carbon content in steel ranges from 0.2% to 2.1% by weight according to size. This research is using experimental method. The object of the study used carbon steel plate st 60 with a specimen size of 28 mm x 18 mm x 3 mm. The specimens tested in this study were 8 specimens that would get different treatments, namely different variations of time and different types of pH. Using the specimen immersion method in a test container with a volume of 50 ml from each test container. A physical test was conducted to determine the differences of carbon steel that had not been corroded with corroded carbon steel, and a weight test to determine the weight ratio of the initial specimen and the final specimen. For immersion in HCl solution with pH 2 the greatest corrosion rate was 22.903 mmpy. Whereas for immersion in NaOH solution with pH 13 the biggest corrosion rate was 0.036 mmpy. For immersion in HCl solution and NaOH solution the greatest corrosion rate occurred on day 2 when testing with HCl solution and the greatest corrosion rate on the 3rd day when testing with NaOH solution. While the smallest corrosion rate of 12,785 mmpy was tested using HCl solution occurred on the 4th day of testing and the smallest corrosion rate of 0,032 mmpy which was tested using NaOH solution occurred on day 1 of the test. Time and pH affect the corrosion rate. The greatest corrosion rate occurs at acidic pH. Keywords : Corrosion, St 60, HCl, NaOH.

Item Type: Skripsi/Thesis (Bachelor)
Uncontrolled Keywords: Korosi, St 60, HCl, NaOH
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Engineering > Mechanical Engineering
Depositing User: Perpus Unim
Date Deposited: 05 Mar 2019 06:18
Last Modified: 04 Apr 2019 02:27
URI: http://repository.unim.ac.id/id/eprint/203