ANALISA NILAI KEKASARAN ALUMUNIUM HASIL PENGECORAN LOGAM DENGAN MEDIA CETAKAN CASTABLE, LOGAM, DAN PASIR

Maulana, Ade, 51704070003 (2021) ANALISA NILAI KEKASARAN ALUMUNIUM HASIL PENGECORAN LOGAM DENGAN MEDIA CETAKAN CASTABLE, LOGAM, DAN PASIR. Bachelor thesis, Universitas Islam Majapahit.

	Text abstrak repository.pdf Restricted to Registered users only Download (1MB) | Request a copy
Preview	Text bab i.pdf Download (90kB) | Preview
	Text bab ii.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text bab iii.pdf Restricted to Registered users only Download (352kB) | Request a copy
	Text bab iv.pdf Restricted to Registered users only Download (600kB) | Request a copy
Preview	Text bab v + dafpus.pdf Download (121kB) | Preview
	Text lampiran.pdf Restricted to Registered users only Download (724kB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui kualitas dari kekasaran suatu material logam hasil pengecoran menggunakan 3 media cetakan yang berbeda yaitu cetakan Castable, Logam dan Pasir. Pada pengujian Surface Roughness Tester didapatkan data sebagai, logam pengecoran media cetakan Pasir rata-rata Ra : 4.105µm, rata-rata Rz : 21.425µm, rata-rata Rq : 5.055µm, logam pengecoran media Castable rata-rata Ra : 7.94µm, rata-rata Rz : 39.37µm, rata-rata Rq : 9.42µm, dan logam pengecoran media cetakan logam (Die Casting) rata-rata Ra : 4.005µm, rata-rata Rz : 20.84µm, rata-rata Rq : 4.96µm. Dari data yang telah teerkumpul dapat disimpulkan nilai uji kekasaran pada logam hasil pengecoran menggunakan cetakan pasir memiliki nila kekasaran paling kecil sedangkan nilai kekasaran paling besar dimiliki oleh logam hasil pengecoran menggunakan media cetakan logam. Kata Kunci : Pengecoran, Media Cetakan, Kekasaran.